PES Hot-Melt Adhesive film

polyester，PES）- PES hot melt adhesive film has washing resistance and temperature resistance, and some products also have flame retardancy. It has good adhesion to materials such as metals, polyester fabrics, PVC, PI films, PC films, and sheets. The melting point of PES hot melt adhesive film is about 90 ° C, 125 ° C, 128 ° C, 130 ° C, 165 ° C, and the recommended pressing temperature for 5 products is about 105-185 ° C. Advantages: Excellent water washing resistance, aging resistance, flame retardancy, and cold resistance

Product type : ?G8116   ?G5216   ?G0906   ?G6016   ?G0216

Applicable Bonding Materials:  ?Polyester fabric textile  ?Laminated Polymer film  ?Rubber-Sponge foam  ?Timber board  ?Paper-Metal sheet

Applicable Fields:  ?Clothing  ?Home textile interior  ?Circulating water treatment  ?Architectural decoration  ?Daily necessities  ?Car interior  ?Luggage industry  ?lamination

Characteristic:

-No elasticity

-Not easy to yellow and age

-Good adhesion to polyester fabric textile, sponge foam and polymer films

-Excellent washing resistance, can be washed many times without opening the glue

Technical data:

********************************************************************

Reference Usgae:

Hot melt adhesive requires hot pressing bonding.

1. Glue two thin and flexible materials, stack (Material 1)/(Hot Melt Adhesive Film)/(Material 2) together, and use a flatbed hot melt bonding machine or flat bed hot melt bonding machine or iron for hot press bonding.The reference temperature is 15-20 degrees above the melting point of the substrate. For example, if the melting point of the mesh adhesive film is 115 degrees, the machine will set the hot press temperature to around 135 degrees and the pressure to 0.2 Mpa for 10 seconds. The specific pressing conditions need to be adjusted according to the actual situation of the customer.When bonding thick metal substrate materials, lay the adhesive(hot melt mesh or film) on the thick metal substrate material and bake them together in an oven at 140 ℃ -160 ℃. After complete melting, the two materialscan be bonded together, and the baking temperature can be adjusted according to the customer's actual situation.

2. Thinner metallic materials can also be pressed by a flat iron press, such as thin aluminum plates, thin copper plates, thin steel plates, etc., and bonded to non-woven fabrics.

Transportation and storage:

Hot melt adhesive film and hot melt adhesive mesh should be handled with care during transportation. Avoid sunlight, rain, high temperature, and high pressure. It is prohibited to use iron hooks for lifting during the loading process

Unload to ensure the packaging is intact and undamaged. Store in a cool, ventilated, dry place with a temperature of 0-30 ℃ (humidity ≤ 70% RH), away from high temperatures, and the stacking height should not exceed 3 layers.

Shelf life: 12-24 months from the date of production.